    飽和泥漿法透水混凝土抗堵性試驗研究
    Experimental Study on Resistance to Clogging of Pervious Concrete by Saturated Slurry Method
    2021年第2期
    透水混凝土;抗堵塞性能;透水損失率;飽和泥漿;連通孔隙率
    Pervious concrete; Resistance to clogging; Loss of permeability; Saturated slurry; Continuous porosity
    2021年第2期
    10.19761/j.1000-4637.2021.02.013.06
    河南省科技發展計劃項目(152102210053)。
    史俊禮1,蔡基偉1,高國防2,付萬長1,周奕菡1,王 顯1
    1.河南大學開封市工程修復與材料循環工程技術研究中心,河南 開封 475004;2.河南建筑材料研究設計院有限責任公司,河南 鄭州 450002

    史俊禮1,蔡基偉1,高國防2,付萬長1,周奕菡1,王 顯1

    史俊禮,蔡基偉,高國防,等.飽和泥漿法透水混凝土抗堵性試驗研究[J].混凝土與水泥制品,2021(2):13-17,22.

    SHI J L,CAI J W,GAO G F,et al.Experimental Study on Resistance to Clogging of Pervious Concrete by Saturated Slurry Method[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):13-17,22.

    瀏覽量:
    1000
    摘 ? 要:以表觀填隙系數為主要控制指標制備了不同強度等級的透水混凝土,分析了透水指標與連通孔隙率的關系。采用黃泛區粉土飽和泥漿作為堵塞介質,測定了預定次數堵塞(淋泥-晾干)循環后的各項透水指標,評價了飽和泥漿對透水混凝土抗堵塞性能的影響。結果表明:透水混凝土各項透水指標與連通孔隙率密切相關;當體系水灰(膠)比為0.24、表觀填隙系數為0.70、高性能減水劑摻量適當時,透水混凝土抗壓強度達到最高(28.3 MPa)且不積漿;經過堵塞循環后,透水混凝土的透水性下降明顯,與摻減水劑試樣相比,未摻減水劑試樣的透水性損失速度快;初始連通孔隙率為10.5%的透水混凝土,經受近30次飽和泥漿的堵塞循環后,透水系數基本衰減到相關規程規定的下限值以下。 Abstract: The samples were prepared by controlling apparent paste-void ratio in pervious concrete, and the relation of permeable parameters to continuous porosity was analyzed. The saturated slurry made of silt in Yellow River Flood Area played a role of clogging medium. The permeable parameters were measured after the samples suffered scheduled clogging (slurry sprinkling - air drying) cycles to evaluate the effect of saturated slurry on resistance of pervious concrete to clogging. The results reveal that the permeable parameters of pervious concrete are closely related to its continuous porosity. The pervious concrete with the highest strength (28.3 MPa) and without paste flow can be prepared with water-cement (binder) ratio of 0.24, proper dosage of superplasticizer and in apparent paste-void ratio of approximate 0.70. The permeability of pervious concrete obviously reduces after clogging cycles. The permeability of pervious concrete samples without superplasticizer generally loses faster than that of samples with superplasticizer. For the pervious concrete with initial continuous porosity of 10.5%, its coefficient of permeability decreases to less than minimum value defined by related specification after nearly 30 clogging cycles.
    英文名 : Experimental Study on Resistance to Clogging of Pervious Concrete by Saturated Slurry Method
    刊期 : 2021年第2期
    關鍵詞 : 透水混凝土;抗堵塞性能;透水損失率;飽和泥漿;連通孔隙率
    Key words : Pervious concrete; Resistance to clogging; Loss of permeability; Saturated slurry; Continuous porosity
    刊期 : 2021年第2期
    DOI : 10.19761/j.1000-4637.2021.02.013.06
    文章編號 :
    基金項目 : 河南省科技發展計劃項目(152102210053)。
    作者 : 史俊禮1,蔡基偉1,高國防2,付萬長1,周奕菡1,王 顯1
    單位 : 1.河南大學開封市工程修復與材料循環工程技術研究中心,河南 開封 475004;2.河南建筑材料研究設計院有限責任公司,河南 鄭州 450002

    史俊禮1,蔡基偉1,高國防2,付萬長1,周奕菡1,王 顯1

    史俊禮,蔡基偉,高國防,等.飽和泥漿法透水混凝土抗堵性試驗研究[J].混凝土與水泥制品,2021(2):13-17,22.

    SHI J L,CAI J W,GAO G F,et al.Experimental Study on Resistance to Clogging of Pervious Concrete by Saturated Slurry Method[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):13-17,22.

    摘要
    參數
    結論
    參考文獻
    引用本文

    摘   要:以表觀填隙系數為主要控制指標制備了不同強度等級的透水混凝土,分析了透水指標與連通孔隙率的關系。采用黃泛區粉土飽和泥漿作為堵塞介質,測定了預定次數堵塞(淋泥-晾干)循環后的各項透水指標,評價了飽和泥漿對透水混凝土抗堵塞性能的影響。結果表明:透水混凝土各項透水指標與連通孔隙率密切相關;當體系水灰(膠)比為0.24、表觀填隙系數為0.70、高性能減水劑摻量適當時,透水混凝土抗壓強度達到最高(28.3 MPa)且不積漿;經過堵塞循環后,透水混凝土的透水性下降明顯,與摻減水劑試樣相比,未摻減水劑試樣的透水性損失速度快;初始連通孔隙率為10.5%的透水混凝土,經受近30次飽和泥漿的堵塞循環后,透水系數基本衰減到相關規程規定的下限值以下。

    Abstract: The samples were prepared by controlling apparent paste-void ratio in pervious concrete, and the relation of permeable parameters to continuous porosity was analyzed. The saturated slurry made of silt in Yellow River Flood Area played a role of clogging medium. The permeable parameters were measured after the samples suffered scheduled clogging (slurry sprinkling - air drying) cycles to evaluate the effect of saturated slurry on resistance of pervious concrete to clogging. The results reveal that the permeable parameters of pervious concrete are closely related to its continuous porosity. The pervious concrete with the highest strength (28.3 MPa) and without paste flow can be prepared with water-cement (binder) ratio of 0.24, proper dosage of superplasticizer and in apparent paste-void ratio of approximate 0.70. The permeability of pervious concrete obviously reduces after clogging cycles. The permeability of pervious concrete samples without superplasticizer generally loses faster than that of samples with superplasticizer. For the pervious concrete with initial continuous porosity of 10.5%, its coefficient of permeability decreases to less than minimum value defined by related specification after nearly 30 clogging cycles.

    掃二維碼用手機看
    未找到相應參數組,請于后臺屬性模板中添加

    (1)對于原生骨料透水混凝土,不摻減水劑時合理的體系水灰(膠)比為0.290左右,摻減水劑時合理的體系水灰(膠)比為0.240左右,水泥漿對骨料空隙的表觀填隙系數為0.70左右,以使透水混凝土在滿足透水要求的條件下獲得最高的強度。
    (2)當體系水灰(膠)比為0.240,表觀填隙系數為0.70時(B1),透水混凝土28 d抗壓強度可達28.3 MPa,且初始透水系數可達1.58 mm/s,可滿足透水混凝土路面透水要求。
    (3)堵塞試驗每經受預定次數(如7次)的堵塞循環后,測試一次透水指標,達到規定的最低透水性能時結束試驗,以經受的堵塞循環次數來評價透水混凝土的抗堵性,不同地區宜用本地域表層土制備飽和泥漿,作為堵塞介質進行堵塞試驗,比較符合工程實際。
    (4)透水混凝土各項透水指標均與連通孔隙率存在正相關性,且存在密切的量化關系。對于初始連通孔隙率10.5%的透水混凝土,經過近30次飽和泥漿堵塞循環后,透水指標基本可衰減到規程規定的下限值以下。
     

    [1] 吳丹潔,詹圣澤,李友華,等.中國特色海綿城市的新興趨勢與實踐研究[J].中國軟科學,2016(1):79-97.

    [2] 俞孔堅,李迪華,袁弘,等.“海綿城市”理論與實踐[J].城市規劃,2015,39(6):26-36.
    [3] 張國強,賴俊.透水混凝土的研究進展綜述[J].廣東建材, 2016,32(8):72-75.
    [4] 中關村材料試驗技術聯盟.透水混凝土試驗方法:T/CSTM 00040—2019[S].北京:冶金工業出版社,2019.
    [5] 崔新壯,張炯,黃丹,等.暴雨作用下透水混凝土路面快速堵塞試驗模擬[J].中國公路學報,2016,29(10):1-11,19.
    [6] 唐靜,趙玉婷,梁美坤,等.防堵塞型透水制品的制備與性能研究[J].土木與環境工程學報(中英文),2019,41(4):137-142.
    [7] ELANGO K S,REVATHI V.Infiltration and clogging characteristics of pervious concrete[J].Asian Journal of Civil Engineering,2019(20):1119-1127.
    [8] 中華人民共和國住房和城鄉建設部,國家市場監督管理總局.混凝土物理力學性能試驗方法標準:GB/T 50081—2019[S].北京:中國建筑工業出版社,2019.
    [9] 中華人民共和國建設部.普通混凝土用砂、石質量及檢驗方法標準:JGJ 52—2006[S].北京:中國建筑工業出版社,2006.
    [10] 中華人民共和國質量監督檢驗檢疫總局,國家標準化管理委員會.降水量等級:GB/T 28592—2012[S].北京:中國標準出版社,2012.
    [11] 王其英,仝文偉,李姝霞,等.開封近50年暴雨、大暴雨時空分布特征分析[J].河南科學,2010,28(10):1322-1326.
    [12] 陳欣欣,袁建文.開封市“2018.8.18”暴雨調查分析[J].河南水利與南水北調,2018(11):32-34.
    [13] 中華人民共和國住房和城鄉建設部.透水水泥混凝土路面技術規程:CJJ/T 135—2009[S].北京:中國建筑工業出版社,2010.
    [14] 中國天氣網.城市氣候—開封[EB/OL].(2019-12-19)[2020-04-15].http://henan.weather.com.cn/hnqh/dsqh/kfqh.shtml.

    史俊禮,蔡基偉,高國防,.飽和泥漿法透水混凝土抗堵性試驗研究[J].混凝土與水泥制品,2021(2):13-17,22.

    SHI J L,CAI J W,GAO G F,et al.Experimental Study on Resistance to Clogging of Pervious Concrete by Saturated Slurry Method[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):13-17,22.

    相關文件

    暫時沒有內容信息顯示
    請先在網站后臺添加數據記錄。

    關注《混凝土與水泥制品》

    總訪問量 468,401   網站統計

    官方微信公眾號關閉
    蘇州混凝土水泥制品研究院有限公司

    關于我們    |    聯系我們    |    訂購雜志    |    回到頂部

    版權所有:中國混凝土與水泥制品網  蘇ICP備10086386號   網站建設:中企動力 蘇州

    版權所有:中國混凝土與水泥制品網

    蘇ICP備10086386號

    網站建設:中企動力 蘇州

    国产偷窥摄综合色区
      <table id="qrkot"><ruby id="qrkot"></ruby></table>
    1. <acronym id="qrkot"></acronym>
    2. <tr id="qrkot"><s id="qrkot"></s></tr>
    3. <table id="qrkot"><option id="qrkot"></option></table>
    4. <big id="qrkot"><ruby id="qrkot"></ruby></big>
    5. <track id="qrkot"></track>