    珊瑚砂水下不分散混凝土性能試驗研究
    Experimental Study on Anti-washout Underwater Concrete with Coral Sand
    2021年第2期
    珊瑚砂;絮凝劑;不分散混凝土;抗壓強度;水陸強度比
    Coral sand; Anti-washout admixture; Anti-washout concrete; Compressive strength; Underwater/in-air strength ratio
    2021年第2期
    10.19761/j.1000-4637.2021.02.027.05
    廖紹華
    中石化石油工程設計有限公司,山東 東營 257026

    廖紹華

    廖紹華.珊瑚砂水下不分散混凝土性能試驗研究[J].混凝土與水泥制品,2021(2):27-31.

    LIAO S H.Experimental Study on Anti-washout Underwater Concrete with Coral Sand [J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):27-31.

    瀏覽量:
    1000
    摘 ? 要:研究了水泥用量、絮凝劑摻量、砂率對海水拌和珊瑚砂水下不分散混凝土性能的影響。結果表明:珊瑚砂水下不分散混凝土單位用水量為235~283 kg/m3時,砂率對單位用水量的影響最為顯著,用水量隨砂率增加而增大;水泥用量為400~490 kg/m3時,28 d抗壓強度在26~39 MPa之間,可配制C20~C30水下不分散混凝土;水泥用量對抗壓強度的影響最為顯著,強度隨水泥用量的增加而增大;水陸強度比隨水泥和絮凝劑摻量增加而增大。 Abstract: The effects of cement dosage, anti-washout admixture dosage and sand rate on the performance of underwater sand-dispersed concrete with coral sand were studied. The results show when the water consumption of the anti-washout concrete is between 235~283 kg/m3, the sand rate has the most significant effect on the unit water consumption. With the water consumption increasing, the sand rate increases significantly. When the cement dosage is 400~490 kg/m3, the 28 d compressive strength of underwater concrete is between 26~39 MPa, and C20~C30 anti-washout concrete can be prepared. The amount of cement is the most significant in compressive strength, and the strength increases with increasing amount of cement. At the same time, the underwater/in-air strength ratio increases as the amount of cement and anti-washout admixture increases.
    英文名 : Experimental Study on Anti-washout Underwater Concrete with Coral Sand
    刊期 : 2021年第2期
    關鍵詞 : 珊瑚砂;絮凝劑;不分散混凝土;抗壓強度;水陸強度比
    Key words : Coral sand; Anti-washout admixture; Anti-washout concrete; Compressive strength; Underwater/in-air strength ratio
    刊期 : 2021年第2期
    DOI : 10.19761/j.1000-4637.2021.02.027.05
    文章編號 :
    基金項目 :
    作者 : 廖紹華
    單位 : 中石化石油工程設計有限公司,山東 東營 257026

    廖紹華

    廖紹華.珊瑚砂水下不分散混凝土性能試驗研究[J].混凝土與水泥制品,2021(2):27-31.

    LIAO S H.Experimental Study on Anti-washout Underwater Concrete with Coral Sand [J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):27-31.

    摘要
    參數
    結論
    參考文獻
    引用本文

    摘   要:研究了水泥用量、絮凝劑摻量、砂率對海水拌和珊瑚砂水下不分散混凝土性能的影響。結果表明:珊瑚砂水下不分散混凝土單位用水量為235~283 kg/m3時,砂率對單位用水量的影響最為顯著,用水量隨砂率增加而增大;水泥用量為400~490 kg/m3時,28 d抗壓強度在26~39 MPa之間,可配制C20~C30水下不分散混凝土;水泥用量對抗壓強度的影響最為顯著,強度隨水泥用量的增加而增大;水陸強度比隨水泥和絮凝劑摻量增加而增大。

    Abstract: The effects of cement dosage, anti-washout admixture dosage and sand rate on the performance of underwater sand-dispersed concrete with coral sand were studied. The results show when the water consumption of the anti-washout concrete is between 235~283 kg/m3, the sand rate has the most significant effect on the unit water consumption. With the water consumption increasing, the sand rate increases significantly. When the cement dosage is 400~490 kg/m3, the 28 d compressive strength of underwater concrete is between 26~39 MPa, and C20~C30 anti-washout concrete can be prepared. The amount of cement is the most significant in compressive strength, and the strength increases with increasing amount of cement. At the same time, the underwater/in-air strength ratio increases as the amount of cement and anti-washout admixture increases.

    掃二維碼用手機看
    未找到相應參數組,請于后臺屬性模板中添加

    (1)珊瑚砂水下不分散混凝土的單位用水量為235~283 kg/m3,砂率對單位用水量的影響最為顯著,單位用水量隨砂率增加而增大。影響用水量因素的大小順序為:砂率>單位水泥用量>絮凝劑摻量。
    (2)珊瑚砂水下不分散混凝土的水泥用量在400~490 kg/m3時,混凝土28 d水下抗壓強度在26.0~39.1 MPa之間。水泥用量增大,陸地和水下抗壓強度均增加。影響強度因素的大小順序為:單位水泥用量>砂率>絮凝劑摻量。
    (3)隨著絮凝劑摻量的增加,7 d和28 d水陸強度比增大;絮凝劑摻量可控制在12~16 kg/m3。砂率對7 d水陸強度比的影響呈先高后低的趨勢,而對28 d水陸強度比的影響則不明顯。隨著水泥用量的增加,7 d和28 d水陸強度比整體呈現增大的趨勢。影響7 d水陸強度比的因素重要性程度為:單位水泥用量>絮凝劑摻量>砂率;影響28 d水陸強度比的因素重要性程度則為:絮凝劑摻量>單位水泥用量>砂率。

    [1] 王新志.南沙群島珊瑚礁工程地質特性及大型工程建設可行性研究[D].武漢:中國科學院研究生院武漢巖土力學研究所,2008.
    [2] 孫宗勛.南沙群島珊瑚砂工程性質研究[J].熱帶海洋,2000,19(2):1-8.
    [3] 李林.珊瑚混凝土基本特性研究[D].南寧:廣西大學,2012.
    [4] 丁沙.珊瑚砂混凝土配制技術研究[J].建材世界,2016(2): 15-20.
    [5] 陳兆林,唐筱寧,孫國峰,等.海水拌養混凝土耐久性試驗與應用[J].海洋工程,2008(4):102-106.
    [6] 韋灼彬,唐軍務,王文忠.水下不分散混凝土性能的實驗研究[J].混凝土,2012(2):124-126.
    [7] 蔣正武,周文宗.水下抗分散混凝土的性能研究[J].建筑材料學報,2000(6):129-134.
    [8] 馮士明,沈良君,胡德華,等.水下不分散混凝土在核電取水口工程中的應用[J].混凝土,2001(8):6-8.
    [9] 劉巖.水下不分散混凝土在大連碼頭修復中的應用[J].水運工程,2003(6):29,43.
    [10] 水下不分散混凝土在三峽工程中的應用[J].混凝土,2006(12):78-80.
    [11] 中華人民共和國住房和城鄉建設部.普通混凝土配合比設計規程:JGJ 55—2011[S].北京:中國建筑出版社,2011.

    廖紹華.珊瑚砂水下不分散混凝土性能試驗研究[J].混凝土與水泥制品,2021(2):27-31.

    LIAO S H.Experimental Study on Anti-washout Underwater Concrete with Coral Sand [J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):27-31.

    相關文件

    暫時沒有內容信息顯示
    請先在網站后臺添加數據記錄。

    關注《混凝土與水泥制品》

    總訪問量 468,401   網站統計

    官方微信公眾號關閉
    蘇州混凝土水泥制品研究院有限公司

    關于我們    |    聯系我們    |    訂購雜志    |    回到頂部

    版權所有:中國混凝土與水泥制品網  蘇ICP備10086386號   網站建設:中企動力 蘇州

    版權所有:中國混凝土與水泥制品網

    蘇ICP備10086386號

    網站建設:中企動力 蘇州

    国产偷窥摄综合色区
      <table id="qrkot"><ruby id="qrkot"></ruby></table>
    1. <acronym id="qrkot"></acronym>
    2. <tr id="qrkot"><s id="qrkot"></s></tr>
    3. <table id="qrkot"><option id="qrkot"></option></table>
    4. <big id="qrkot"><ruby id="qrkot"></ruby></big>
    5. <track id="qrkot"></track>