    高強硅酸鹽陶?;炷恋闹苽浼靶阅苎芯?/div>
    Study on Preparation and Properties of High-strength Silicate Ceramsite Concrete
    2022年第5期
    陶粒;高強輕骨料混凝土;頁巖陶砂;水膠比;抗壓強度;干表觀密度
    Ceramsite; High-strength lightweight aggregate concrete; Shale ceramsite sand; Water-binder ratio; Compressive strength; Dry apparent density
    2022年第5期
    10.19761/j.1000-4637.2022.05.067.05
    上海市浦江人才計劃資助項目(20PJ1417600);上海市科學技術委員會資助項目(18DZ2282600)。
    朱 然1,2,王圣怡1,2,占羿箭1,2
    1.上海建工集團股份有限公司,上海 200080;2.上海高大結構高性能混凝土工程技術研究中心, 上海 201114

    朱 然1,2,王圣怡1,2,占羿箭1,2

    朱然,王圣怡,占羿箭.高強硅酸鹽陶?;炷恋闹苽浼靶阅苎芯縖J].混凝土與水泥制品,2022(5):67-71.

    ZHU R,WANG S Y,ZHAN Y J.Study on Preparation and Properties of High-strength Silicate Ceramsite Concrete[J].China Concrete and Cement Products,2022(5):67-71.

    瀏覽量:
    1000
    摘 ? 要:對陶粒、陶砂進行預濕處理,并將其用于配制高強硅酸鹽陶?;炷?,研究了水膠比、漂珠摻量、陶砂取代率對高強硅酸鹽陶?;炷列阅艿挠绊?。結果表明:預吸水陶粒、陶砂具備改善界面性能、內養護等多重作用,可有效提高輕骨料混凝土的強度;水膠比是決定輕骨料混凝土強度的關鍵因素,隨著水膠比的降低,輕骨料混凝土的強度增長明顯;減重材料如漂珠應謹慎使用,使用時應設置合理的應用區間,避免輕骨料混凝土中的水分含量出現較大波動。 Abstract: The ceramsite and ceramic sand were pre-wetted and used to prepare high-strength silicate ceramsite concrete. The effects of water-binder ratio, fly ash cenosphere content and ceramic sand replacement rate on the properties of high-strength silicate ceramsite concrete were studied. The results show that pre-absorbent ceramsite and ceramic sand have multiple functions such as improving the interface performance and internal curing, which can effectively increase the strength of lightweight aggregate concrete. The water-binder ratio is the key factor in determining the strength of lightweight aggregate concrete. As the water-binder ratio decreases, the strength of lightweight aggregate concrete increases significantly. Weight-reducing materials such as fly ash cenosphere should be used with caution, and a reasonable application interval should be set to avoid large fluctuations in the moisture content of lightweight aggregate concrete.
    英文名 : Study on Preparation and Properties of High-strength Silicate Ceramsite Concrete
    刊期 : 2022年第5期
    關鍵詞 : 陶粒;高強輕骨料混凝土;頁巖陶砂;水膠比;抗壓強度;干表觀密度
    Key words : Ceramsite; High-strength lightweight aggregate concrete; Shale ceramsite sand; Water-binder ratio; Compressive strength; Dry apparent density
    刊期 : 2022年第5期
    DOI : 10.19761/j.1000-4637.2022.05.067.05
    文章編號 :
    基金項目 : 上海市浦江人才計劃資助項目(20PJ1417600);上海市科學技術委員會資助項目(18DZ2282600)。
    作者 : 朱 然1,2,王圣怡1,2,占羿箭1,2
    單位 : 1.上海建工集團股份有限公司,上海 200080;2.上海高大結構高性能混凝土工程技術研究中心, 上海 201114

    朱 然1,2,王圣怡1,2,占羿箭1,2

    朱然,王圣怡,占羿箭.高強硅酸鹽陶?;炷恋闹苽浼靶阅苎芯縖J].混凝土與水泥制品,2022(5):67-71.

    ZHU R,WANG S Y,ZHAN Y J.Study on Preparation and Properties of High-strength Silicate Ceramsite Concrete[J].China Concrete and Cement Products,2022(5):67-71.

    摘要
    參數
    結論
    參考文獻
    引用本文

    摘   要:對陶粒、陶砂進行預濕處理,并將其用于配制高強硅酸鹽陶?;炷?,研究了水膠比、漂珠摻量、陶砂取代率對高強硅酸鹽陶?;炷列阅艿挠绊?。結果表明:預吸水陶粒、陶砂具備改善界面性能、內養護等多重作用,可有效提高輕骨料混凝土的強度;水膠比是決定輕骨料混凝土強度的關鍵因素,隨著水膠比的降低,輕骨料混凝土的強度增長明顯;減重材料如漂珠應謹慎使用,使用時應設置合理的應用區間,避免輕骨料混凝土中的水分含量出現較大波動。

    Abstract: The ceramsite and ceramic sand were pre-wetted and used to prepare high-strength silicate ceramsite concrete. The effects of water-binder ratio, fly ash cenosphere content and ceramic sand replacement rate on the properties of high-strength silicate ceramsite concrete were studied. The results show that pre-absorbent ceramsite and ceramic sand have multiple functions such as improving the interface performance and internal curing, which can effectively increase the strength of lightweight aggregate concrete. The water-binder ratio is the key factor in determining the strength of lightweight aggregate concrete. As the water-binder ratio decreases, the strength of lightweight aggregate concrete increases significantly. Weight-reducing materials such as fly ash cenosphere should be used with caution, and a reasonable application interval should be set to avoid large fluctuations in the moisture content of lightweight aggregate concrete.

    掃二維碼用手機看
    未找到相應參數組,請于后臺屬性模板中添加

    (1)混凝土立方體抗壓試件的破壞形態表明,陶粒殼層的硅鋁玻璃體參與了二次水化反應,使基體與骨料之間的黏結性能增強。預濕24 h后的陶粒、陶砂攜帶了部分附加水,使基體內的水化更為充分,從而提高了高強輕骨料混凝土的強度。
    (2)與普通混凝土類似,水膠比仍是決定高強輕骨料混凝土強度的關鍵因素。隨著水膠比的降低,高強輕骨料混凝土的強度增長明顯。同時,水膠比的降低減少了高強輕骨料混凝土內的孔洞數量,從而提高了高強輕骨料混凝土的干表觀密度。因此,在高強輕骨料混凝土的配合比設計環節,應注意尋求強度與干表觀密度的平衡點,以滿足工程與設計需求。
    (3)作為減輕劑的漂珠雖可優化混凝土的材性,但其吸水效應明顯。漂珠摻量過高時,混凝土拌和物的流動性喪失,嚴重影響了高強輕骨料混凝土的力學性能,應謹慎使用。
    (4)陶砂的吸水率較高,合適取代率下,陶砂可有效提高混凝土漿體的包裹性能,減少骨料-基材界面缺陷,從而提高混凝土的整體性能。使用陶砂時,應設置合理的使用區間,以避免混凝土出現離析或其他不穩定現象。
    (5)在高強輕骨料混凝土的配合比設計與應用中,拌和水用量與輕質材料的吸水、釋水性能是控制的關鍵環節。因此,在試配優化前,需做好各類多孔輕質材料吸水、保水、釋水性能的研究工作,從而為取得合理、優質的配合比奠定基礎。

    [1] 張寶生,孔麗娟,袁杰,等.輕骨料預濕程度對混合骨料混凝土力學性能的影響[J].混凝土,2006(10):24-26,30.
    [2] 王志新,陳鶴云,劉光華,等.超輕水泥混凝土在工程中的應用[J].混凝土與水泥制品,1999(1):42-43.
    [3] 劉喜,史尚冕,趙天俊,等.輕骨料混凝土彈性模量計算模型分析[J].硅酸鹽通報,2017,36(7):2192-2196.
    [4] 郭旭東,戴毓.透明輕骨料混凝土制備及耐久性研究[J].混凝土與水泥制品,2020(2):82-85.
    [5] 侯景鵬,劉俊龍,史巍,等.雙摻礦物摻合料輕骨料混凝土性能試驗研究[J].混凝土與水泥制品,2020(3):70-72,90.
    [6] 穆龍飛,李思琪,馮竟竟,等.預濕骨料對陶?;炷列阅苡绊懙脑囼炑芯縖J].混凝土與水泥制品,2019(11):66-69.
    [7] 中華人民共和國住房和城鄉建設部.輕骨料混凝土應用技術標準:JGJ/T 12—2019[S].北京:中國建筑工業出版社,2019.
    [8] CHANDRA S,BERNTSSON L.Lightweight Aggregate Concrete[M].New York:Noyes Publications,2002.
    [9] 劉增晨.高強輕集料混凝土的配制與性能研究[D].天津:天津大學,2016.
    [10] 楊秀麗,崔崇,崔曉昱,等.殼層增強人造硅酸鹽骨料性能[J].科技導報,2014,32(25):26-31.
    [11] MA H,CUI C,MA W,et al.Enhancement Mechanism of New Type Autoclaved Calcium Carbide Residue Shell-aggregate on Concrete[J].Cement and Concrete Composites,2016,72:146-154.
    [12] WANG D,CUI C,CHEN X F,et al.Characteristics of Autoclaved Lightweight Aggregates with Quartz Tailings and Its Effect on the Mechanical Properties of Concrete[J].Construction and Building Materials,2020,262:120110.
    [13] 楊秀麗,崔崇,崔曉昱,等.高性能人造硅酸鹽骨料及其混凝土的性能研究[J].科技導報,2014,32(23):50-54.
    [14] 王利東,李珠,趙林,等.漂珠級配對保溫混凝土性能的影響試驗研究[J].新型建筑材料,2016,43(9):102-104.
    [15] 董素芹.漂珠代砂混凝土性能的試驗研究[J].混凝土,2017(7):96-98.
    [16] SATPATHY H,PATEL S,NAYAK A.Development of Sustainable Lightweight Concrete Using Fly Ash Cenosphere and Sintered Fly Ash Aggregate[J].Construction and Building Materials,2019,202:636-655.

    朱然,王圣怡,占羿箭.高強硅酸鹽陶?;炷恋闹苽浼靶阅苎芯?/font>[J].混凝土與水泥制品,2022(5):67-71.

    ZHU R,WANG S Y,ZHAN Y J.Study on Preparation and Properties of High-strength Silicate Ceramsite Concrete[J].China Concrete and Cement Products,2022(5):67-71.

    相關文件

    暫時沒有內容信息顯示
    請先在網站后臺添加數據記錄。

    關注《混凝土與水泥制品》

    總訪問量 468,401   網站統計

    官方微信公眾號關閉
    蘇州混凝土水泥制品研究院有限公司

    關于我們    |    聯系我們    |    訂購雜志    |    回到頂部

    版權所有:中國混凝土與水泥制品網  蘇ICP備10086386號   網站建設:中企動力 蘇州

    版權所有:中國混凝土與水泥制品網

    蘇ICP備10086386號

    網站建設:中企動力 蘇州

    国产偷窥摄综合色区
      <table id="qrkot"><ruby id="qrkot"></ruby></table>
    1. <acronym id="qrkot"></acronym>
    2. <tr id="qrkot"><s id="qrkot"></s></tr>
    3. <table id="qrkot"><option id="qrkot"></option></table>
    4. <big id="qrkot"><ruby id="qrkot"></ruby></big>
    5. <track id="qrkot"></track>