    納米C-S-H對固硫灰蒸壓加氣混凝土水化產物形成的影響
    Effect of Nano-C-S-H on the Formation of Hydration Products of Autoclaved Aerated Concrete with Circulating Fluidized Bed Fly Ash
    2022年第5期
    納米C-S-H;固硫灰;蒸壓加氣混凝土;抗壓強度;干密度;水化產物
    Nano C-S-H; Circulating fluidized bed fly ash; Autoclaved aerated concrete; Compressive strength; Dry density; Hydration product
    2022年第5期
    10.19761/j.1000-4637.2022.05.072.05
    廣西重點研發計劃項目(桂科AB19245046);廣西科技創新驅動發展重大專項項目(桂科AA17202001)。
    柏秀奎1,林俊豪2,曹德光1,韋炫辰1,歐天安2,潘榮偉2,李乘光3
    1.廣西大學 資源環境與材料學院,廣西 南寧 530004;2.廣西建筑材料科學研究設計院有限公司, 廣西 南寧 530004;3.廣西都安西江魚峰水泥有限公司,廣西 河池 547000

    柏秀奎1,林俊豪2,曹德光1,韋炫辰1,歐天安2,潘榮偉2,李乘光3

    柏秀奎,林俊豪,曹德光,等.納米C-S-H對固硫灰蒸壓加氣混凝土水化產物形成的影響[J].混凝土與水泥制品,2022(5):72-76.

    BAI X K,LIN J H,CAO D G,et al.Effect of Nano-C-S-H on the Formation of Hydration Products of Autoclaved Aerated Concrete with Circulating Fluidized Bed Fly Ash[J].China Concrete and Cement Products,2022(5):72-76.

    瀏覽量:
    1000
    摘 ? 要:通過強度、干密度測試以及XRD、FTIR、SEM分析,研究了納米C-S-H對固硫灰蒸壓加氣混凝土性能及水化產物的影響。結果表明:隨著納米C-S-H摻量的增加,蒸壓加氣混凝土的干密度和抗壓強度均呈先增后降的趨勢,且當納米C-S-H摻量為3%時,蒸壓加氣混凝土的抗壓強度最大,較空白組提高了13.2%;在蒸壓養護條件下,納米C-S-H的摻入一方面促進了體系中的Ca(OH)2與固硫灰中的活性SiO2和Al2O3反應,形成了更多的托貝莫來石和C-S-H凝膠,另一方面加速了托貝莫來石和C-S-H凝膠的生長速度,形成了尺寸更大的反應產物;納米C-S-H的摻入降低了蒸壓加氣混凝土中的孔洞率,提高了蒸壓加氣混凝土的密實度和強度;固硫灰中的三種主要物相與Ca(OH)2的蒸壓反應活性大小為薄片疊層狀的黏土礦物熱分解產物最高,帶棱角粒狀的石英顆粒次之,球狀的鋁硅酸鈣物相最低。 Abstract: The effects of nano-C-S-H on properties and hydration products of autoclaved aerated concrete with circulating fluidized bed fly ash were studied by strength, dry density tests and XRD, FTIR and SEM analysis. The results show that the dry density and compressive strength of autoclaved aerated concrete increase first and then decrease with the increase of nano-C-S-H content, and the compressive strength of autoclaved aerated concrete reaches the maximum when the nano-C-S-H content is 3%, which is 13.2% higher than that of blank group. Under the autoclastic curing condition, the addition of nano-C-S-H promotes the reaction of Ca(OH)2 in the system with active SiO2 and Al2O3 in the circulating fluidized bed fly ash, forming more tobermorite and C-S-H gel, and accelerates the growth rate of tobermorite and C-S-H gel, forming reaction products with larger size. The addition of nano-C-S-H reduces the porosity of autoclaved aerated concrete, and improves the density and compressive strength of autoclaved aerated concrete. The autoclaved reaction activity of the three main phases in the circulating fluidized bed fly ash with Ca(OH)2 is that the laminated products of clay are the highest, followed by the angular granular quartz particles, and the spherical phase of calcium aluminosilicate is the lowest.
    英文名 : Effect of Nano-C-S-H on the Formation of Hydration Products of Autoclaved Aerated Concrete with Circulating Fluidized Bed Fly Ash
    刊期 : 2022年第5期
    關鍵詞 : 納米C-S-H;固硫灰;蒸壓加氣混凝土;抗壓強度;干密度;水化產物
    Key words : Nano C-S-H; Circulating fluidized bed fly ash; Autoclaved aerated concrete; Compressive strength; Dry density; Hydration product
    刊期 : 2022年第5期
    DOI : 10.19761/j.1000-4637.2022.05.072.05
    文章編號 :
    基金項目 : 廣西重點研發計劃項目(桂科AB19245046);廣西科技創新驅動發展重大專項項目(桂科AA17202001)。
    作者 : 柏秀奎1,林俊豪2,曹德光1,韋炫辰1,歐天安2,潘榮偉2,李乘光3
    單位 : 1.廣西大學 資源環境與材料學院,廣西 南寧 530004;2.廣西建筑材料科學研究設計院有限公司, 廣西 南寧 530004;3.廣西都安西江魚峰水泥有限公司,廣西 河池 547000

    柏秀奎1,林俊豪2,曹德光1,韋炫辰1,歐天安2,潘榮偉2,李乘光3

    柏秀奎,林俊豪,曹德光,等.納米C-S-H對固硫灰蒸壓加氣混凝土水化產物形成的影響[J].混凝土與水泥制品,2022(5):72-76.

    BAI X K,LIN J H,CAO D G,et al.Effect of Nano-C-S-H on the Formation of Hydration Products of Autoclaved Aerated Concrete with Circulating Fluidized Bed Fly Ash[J].China Concrete and Cement Products,2022(5):72-76.

    摘要
    參數
    結論
    參考文獻
    引用本文

    摘   要:通過強度、干密度測試以及XRD、FTIR、SEM分析,研究了納米C-S-H對固硫灰蒸壓加氣混凝土性能及水化產物的影響。結果表明:隨著納米C-S-H摻量的增加,蒸壓加氣混凝土的干密度和抗壓強度均呈先增后降的趨勢,且當納米C-S-H摻量為3%時,蒸壓加氣混凝土的抗壓強度最大,較空白組提高了13.2%;在蒸壓養護條件下,納米C-S-H的摻入一方面促進了體系中的Ca(OH)2與固硫灰中的活性SiO2和Al2O3反應,形成了更多的托貝莫來石和C-S-H凝膠,另一方面加速了托貝莫來石和C-S-H凝膠的生長速度,形成了尺寸更大的反應產物;納米C-S-H的摻入降低了蒸壓加氣混凝土中的孔洞率,提高了蒸壓加氣混凝土的密實度和強度;固硫灰中的三種主要物相與Ca(OH)2的蒸壓反應活性大小為薄片疊層狀的黏土礦物熱分解產物最高,帶棱角粒狀的石英顆粒次之,球狀的鋁硅酸鈣物相最低。

    Abstract: The effects of nano-C-S-H on properties and hydration products of autoclaved aerated concrete with circulating fluidized bed fly ash were studied by strength, dry density tests and XRD, FTIR and SEM analysis. The results show that the dry density and compressive strength of autoclaved aerated concrete increase first and then decrease with the increase of nano-C-S-H content, and the compressive strength of autoclaved aerated concrete reaches the maximum when the nano-C-S-H content is 3%, which is 13.2% higher than that of blank group. Under the autoclastic curing condition, the addition of nano-C-S-H promotes the reaction of Ca(OH)2 in the system with active SiO2 and Al2O3 in the circulating fluidized bed fly ash, forming more tobermorite and C-S-H gel, and accelerates the growth rate of tobermorite and C-S-H gel, forming reaction products with larger size. The addition of nano-C-S-H reduces the porosity of autoclaved aerated concrete, and improves the density and compressive strength of autoclaved aerated concrete. The autoclaved reaction activity of the three main phases in the circulating fluidized bed fly ash with Ca(OH)2 is that the laminated products of clay are the highest, followed by the angular granular quartz particles, and the spherical phase of calcium aluminosilicate is the lowest.

    掃二維碼用手機看
    未找到相應參數組,請于后臺屬性模板中添加

    (1)納米C-S-H促進了固硫灰蒸壓加氣混凝土中C-S-H凝膠和托貝莫來石的生成。蒸壓加氣混凝土的抗壓強度和干密度隨納米C-S-H摻量的增加呈先增大后減小的趨勢,當納米C-S-H摻量為3%時,蒸壓加氣混凝土的抗壓強度最大,較空白組提高了13.2%。
    (2)在蒸壓養護條件下,納米C-S-H一方面促進了水泥水化,提高了反應體系的堿度;另一方面降低了反應勢壘,促進了固硫灰中活性SiO2和Al2O3與Ca(OH)2的反應,使蒸壓加氣混凝土中的SiO2衍射峰強度顯著降低,而托貝莫來石和C-S-H凝膠衍射峰增強,反應產物數量明顯增加,尺寸明顯增大。
    (3)納米C-S-H改變了蒸壓反應產物的顆粒尺寸和分布狀態,改變了顆粒間的堆積模式, 提高了蒸壓加氣混凝土的密實度,從而導致蒸壓加氣混凝土的抗壓強度提高。
    (4)固硫灰中的三種主要物相與Ca(OH)2的蒸壓反應活性大小為:薄片疊層狀的黏土礦物熱分解產物>帶棱角粒狀的石英顆粒>球狀的鋁硅酸鈣物相。其中,球狀顆粒物相容易殘留在蒸壓加氣混凝土中。

    [1] 宋遠明,錢覺時,王智,等.固硫灰渣的微觀結構與火山灰反應特性[J].硅酸鹽學報,2006,34(12):1542-1546.
    [2] 陳振文,朱國瑞,王奇,等.蒸壓條件對固硫灰加氣混凝土性能影響研究[J].粉煤灰綜合利用,2015(5):19-21,24.
    [3] 袁玉環,李蒙蒙,李雪,等.鈣硅比對固硫灰加氣混凝土性能影響研究[J].粉煤灰綜合利用,2014(3):9-11.
    [4] 閆京勇,王玉燕,周少龍,等.水料比對固硫灰加氣混凝土性能的影響[J].粉煤灰綜合利用,2017(1):12-14,19.
    [5] 肖長根,石海信,王榮健,等.免蒸壓加氣混凝土砌塊研究現狀與發展趨勢[J].廣東化工,2021,48(9):158-161.
    [6] 張克.流化床固硫灰渣配制的水泥與混凝土性能分析[D].重慶:重慶大學,2012.
    [7] XIA Y,YAN Y,HU Z.Utilization of Circulating Fluidized Bed Fly Ash in Preparing Non -autoclaved Aerated Concrete Production[J].Construction and Building Materials,2013(47):1461-1467.
    [8] 徐正坦,翁仁貴.蒸壓流化床粉煤灰混凝土砌塊養護優化設計[J].長春工業大學學報(自然科學版),2012,33(4):469-472.
    [9] 楊利遠,萬惠文,李杰.利用磷尾礦制備加氣混凝土工藝參數的探索研究[J].武漢理工大學學報,2011,33(9):41-44.
    [10] 劉春英,任國盛,高小建.新型復合早強劑對水泥砂漿力學性能的影響[J].硅酸鹽通報,2020,39(12):3806-3811.
    [11] JOUDI-BAHRI I,LECOMTE A,OUEZDOU M B,et al.Use of Limestone Sands and Fillers in Concrete Without Superplasticizer[J].Cement and Concrete Composites,2012,34(6):771-780.
    [12] 韋迎春,錢覺時,張志偉,等.蒸壓養護對固硫灰渣膨脹性能的影響研究[J].土木建筑與環境工程,2010,32(6):142-146.
    [13] 張朝陽,蔡熠,孔祥明,等.納米C-S-H對水泥水化、硬化漿體孔結構及混凝土強度的影響[J].硅酸鹽學報,2019,47(5):585-593.
    [14] 曹德光,蘇達根,楊占印,等.偏高嶺石的微觀結構與鍵合反應能力[J].礦物學報,2004,24(4):366-372.
    [15] 華中師范學院化學系.有機化合物波譜分析[M].北京:化學工業出版社,1981.
    [16] 毛奎,蔡亮,吳小文,等.幾種典型鐵尾礦制備加氣混凝土性能及水化機理研究[J].硅酸鹽通報,2019,38(12):3719-3725.

    柏秀奎,林俊豪,曹德光,.納米C-S-H對固硫灰蒸壓加氣混凝土水化產物形成的影響[J].混凝土與水泥制品,2022(5):72-76.

    BAI X K,LIN J H,CAO D G,et al.Effect of Nano-C-S-H on the Formation of Hydration Products of Autoclaved Aerated Concrete with Circulating Fluidized Bed Fly Ash[J].China Concrete and Cement Products,2022(5):72-76.

    相關文件

    暫時沒有內容信息顯示
    請先在網站后臺添加數據記錄。

    關注《混凝土與水泥制品》

    總訪問量 468,401   網站統計

    官方微信公眾號關閉
    蘇州混凝土水泥制品研究院有限公司

    關于我們    |    聯系我們    |    訂購雜志    |    回到頂部

    版權所有:中國混凝土與水泥制品網  蘇ICP備10086386號   網站建設:中企動力 蘇州

    版權所有:中國混凝土與水泥制品網

    蘇ICP備10086386號

    網站建設:中企動力 蘇州

    国产偷窥摄综合色区
      <table id="qrkot"><ruby id="qrkot"></ruby></table>
    1. <acronym id="qrkot"></acronym>
    2. <tr id="qrkot"><s id="qrkot"></s></tr>
    3. <table id="qrkot"><option id="qrkot"></option></table>
    4. <big id="qrkot"><ruby id="qrkot"></ruby></big>
    5. <track id="qrkot"></track>