    堿化稻草纖維對尾砂充填體力學性能的影響
    Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill
    2022年第7期
    尾砂充填體;稻草纖維;堿化處理;抗壓強度;微觀分析
    Tailings backfill; Straw fiber; Alkalization treatment; Compressive strength; Microscopic analysis
    2022年第7期
    10.19761/j.1000-4637.2022.07.060.04
    市校(院所)科技合作項目-市屬高校產學研項目(2019-SG-17)。
    張 競,李 駿
    福州理工學院 應用科學與工程學院,福建 福州 350000

    張 競,李 駿

    張競,李駿.堿化稻草纖維對尾砂充填體力學性能的影響[J].混凝土與水泥制品,2022(7):60-63.

    ZHANG J,LI J.Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill[J].China Concrete and Cement Products,2022(7):60-63.

    瀏覽量:
    1000
    摘 ? 要:將經過濃度為4%的NaOH溶液堿化處理過的稻草纖維作為加筋材料用于尾砂充填體試件的制備,研究了灰砂比、堿化稻草纖維的長度和摻量對尾砂充填體試件抗壓強度的影響,并借助掃描電鏡(SEM)從微觀角度分析了堿化稻草纖維的作用機理。結果表明:隨著堿化稻草纖維摻量的增加,試件的抗壓強度下降;隨著堿化稻草纖維長度的增加,試件的抗壓強度先增大后減??;未堿化稻草纖維對試件抗壓強度的降低程度顯著大于堿化稻草纖維;隨著灰砂比的減小,試件的抗壓強度降低。 Abstract: The straw fiber alkalized by 4% NaOH solution was used as reinforcement material for the preparation of tailings backfill specimens. The effects of cement-sand ratio, length and content of alkalized straw fiber on the compressive strength of tailings backfill specimens were studied, and the action mechanism of alkalized straw fiber was analyzed by SEM. The results show that the compressive strength of the specimen decreases with the increase of the alkalized straw fiber content. With the increase of the length of alkalized straw fiber, the compressive strength of the specimen first increases and then decreases. The reduction degree of the compressive strength of the specimen by the non-alkalized straw fiber is significantly greater than that of the alkalized straw fiber. With the decrease of cement sand ratio, the compressive strength of the specimen decreases.
    英文名 : Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill
    刊期 : 2022年第7期
    關鍵詞 : 尾砂充填體;稻草纖維;堿化處理;抗壓強度;微觀分析
    Key words : Tailings backfill; Straw fiber; Alkalization treatment; Compressive strength; Microscopic analysis
    刊期 : 2022年第7期
    DOI : 10.19761/j.1000-4637.2022.07.060.04
    文章編號 :
    基金項目 : 市校(院所)科技合作項目-市屬高校產學研項目(2019-SG-17)。
    作者 : 張 競,李 駿
    單位 : 福州理工學院 應用科學與工程學院,福建 福州 350000

    張 競,李 駿

    張競,李駿.堿化稻草纖維對尾砂充填體力學性能的影響[J].混凝土與水泥制品,2022(7):60-63.

    ZHANG J,LI J.Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill[J].China Concrete and Cement Products,2022(7):60-63.

    摘要
    參數
    結論
    參考文獻
    引用本文

    摘   要:將經過濃度為4%的NaOH溶液堿化處理過的稻草纖維作為加筋材料用于尾砂充填體試件的制備,研究了灰砂比、堿化稻草纖維的長度和摻量對尾砂充填體試件抗壓強度的影響,并借助掃描電鏡(SEM)從微觀角度分析了堿化稻草纖維的作用機理。結果表明:隨著堿化稻草纖維摻量的增加,試件的抗壓強度下降;隨著堿化稻草纖維長度的增加,試件的抗壓強度先增大后減??;未堿化稻草纖維對試件抗壓強度的降低程度顯著大于堿化稻草纖維;隨著灰砂比的減小,試件的抗壓強度降低。

    Abstract: The straw fiber alkalized by 4% NaOH solution was used as reinforcement material for the preparation of tailings backfill specimens. The effects of cement-sand ratio, length and content of alkalized straw fiber on the compressive strength of tailings backfill specimens were studied, and the action mechanism of alkalized straw fiber was analyzed by SEM. The results show that the compressive strength of the specimen decreases with the increase of the alkalized straw fiber content. With the increase of the length of alkalized straw fiber, the compressive strength of the specimen first increases and then decreases. The reduction degree of the compressive strength of the specimen by the non-alkalized straw fiber is significantly greater than that of the alkalized straw fiber. With the decrease of cement sand ratio, the compressive strength of the specimen decreases.

    掃二維碼用手機看
    未找到相應參數組,請于后臺屬性模板中添加

    (1)摻堿化稻草纖維試件的抗壓強度明顯高于摻未堿化稻草纖維試件的抗壓強度。
    (2)隨著堿化稻草纖維長度的增加,尾砂充填體試件的抗壓強度先增大后減??;隨著堿化稻草纖維摻量的增加,尾砂充填體試件的抗壓強度基本呈降低趨勢;隨著灰砂比的減小,尾砂充填體試件的抗壓強度降低。本試驗堿化稻草纖維的最佳長度和摻量分別為10 mm和0.3%,最佳灰砂比為1∶4,此時,尾砂充填體試件的抗壓強度與未摻稻草纖維的空白組相差不大。
    (3)方差分析結果表明,各因素對尾砂充填體試件抗壓強度的影響程度大小為:灰砂比>堿化稻草纖維長度>堿化稻草纖維摻量。

    [1] 王昆,楊鵬,KAREN H E,等.尾礦庫潰壩災害防控現狀及發展[J].工程科學學報,2018(5):526-539.
    [2] 張海波,宋衛東,許英霞.充填采礦技術應用發展及存在問題研究[J].黃金,2010,31(1):23-25.
    [3] 徐文彬,李乾龍,田明明.聚丙烯纖維加筋固化尾砂強度及變形特性[J].工程科學學報,2019(12):1618-1626.
    [4] ROMUALDI J P,MANDEL J A.Tensile Strength of Concrete Affected by Uniformly Distributed and Closely Spaced Short Lengths of Wire Reinforcement[J].ACI Materials Journal,1964,61(6):657-672.
    [5] 喻智,史秀志,陳新,等.用于研究纖維尾砂膠結充填材料單軸壓縮性能的新型人工智能模型(英文)[J].Transactions of Nonferrous Metals Society of China,2021(4):1087-1102.
    [6] 薛改利.摻纖維尾砂充填體多尺度力學特性及損傷演化機理研究[D].北京:北京科技大學,2020.
    [7] 孫位,劉長武,吳帆,等.聚丙烯纖維高水材料力學性能的試驗研究[J].金屬礦山,2018(1):53-57.
    [8] 馬國偉,李之建,易夏瑋,等.纖維增強膏體充填材料的宏細觀試驗[J].北京工業大學學報,2016(3):406-412.
    [9] 趙康,宋宇峰,于祥,等.不同纖維作用下尾砂膠結充填體早期力學特性及損傷本構模型研究[J].巖石力學與工程學報,2022,41(2):282-291.
    [10] 楊凱.稻草纖維粉末混凝土空心砌塊的力學及熱工性能研究[D].綿陽:西南科技大學,2016.
    [11] 張學元,王丹丹,張道明,等.稻草纖維輕骨料混凝土力學性能影響因素研究[J].硅酸鹽通報,2019,38(5):1369-1376.
    [12] 王明江.稻殼/稻草纖維水泥基材料的制備與性能[D].哈爾濱:哈爾濱工業大學,2012.
    [13] 寧淑嬪.夾心秸稈混凝土砌塊導熱及力學性能研究[D].長春:吉林建筑大學,2020.
    [14] 尹如霞.稻草纖維微粒水泥基復合材料抗沖擊性能試驗研究[D].綿陽:西南科技大學,2019.
    [15] 宋學朋.堿化水稻秸稈基尾砂膠結充填體動靜力學性能演化機制研究[D].贛州:江西理工大學,2021.
    [16] 李藝,趙文.混雜纖維混凝土阻裂增韌及耐久性能[M].北京:科學出版社,2012.

    張競,李駿.堿化稻草纖維對尾砂充填體力學性能的影響[J].混凝土與水泥制品,2022(7):60-63.

    ZHANG J,LI J.Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill[J].China Concrete and Cement Products,2022(7):60-63.

    相關文件

    暫時沒有內容信息顯示
    請先在網站后臺添加數據記錄。

    關注《混凝土與水泥制品》

    總訪問量 468,401   網站統計

    官方微信公眾號關閉
    蘇州混凝土水泥制品研究院有限公司

    關于我們    |    聯系我們    |    訂購雜志    |    回到頂部

    版權所有:中國混凝土與水泥制品網  蘇ICP備10086386號   網站建設:中企動力 蘇州

    版權所有:中國混凝土與水泥制品網

    蘇ICP備10086386號

    網站建設:中企動力 蘇州

    国产偷窥摄综合色区
      <table id="qrkot"><ruby id="qrkot"></ruby></table>
    1. <acronym id="qrkot"></acronym>
    2. <tr id="qrkot"><s id="qrkot"></s></tr>
    3. <table id="qrkot"><option id="qrkot"></option></table>
    4. <big id="qrkot"><ruby id="qrkot"></ruby></big>
    5. <track id="qrkot"></track>