Abstract: Concrete with different FNS(Ferronickel slag) contents was prepared, and its compressive strength, splitting tensile strength, elastic modulus and drying shrinkage were tested. The pore structures of the pastes with the same proportions were analyzed by mercury intrusion porosimetry (MIP). The experimental results show that the compressive strength of FNS concrete increases firstly and then decreases as the FNS replacement goes higher, which has a significant correlation with the change of pore structures. When the FNS replacement is over 20%, the development of strength of FNS concretes is slower than that of plain concrete and this difference can be compensated after 90 days’ curing. Moreover, the FNS weakens the splitting tensile strength but improves the elastic modulus of concrete. The FNS can be partly activated by steam curing, but it cannot cover the loss of strength due to the decrease in cement content. FNS concrete with an FNS content less than 20% has a smaller drying shrinkage than plain concrete, which can be attributed to the lower porosity and the higher elastic modulus of concrete.
王申,李保亮,曹瑞林,等.鎳鐵渣混凝土的力學性能、干縮行為及其與漿體孔結構的關系[J].混 凝土與水泥制品,2020(1):1-5. WANG S,LI B l,CAO R L,et al.Mechanical Properties, Drying Shrinkage and Their Relation with Pore Structure of Concrete with Ferronickel Slag[J].China Concrete and Cement Products,2020(1):1-5.